The study of adhesion and nanomechanical properties of DLC films deposited on tool steels

In this study, thin diamond-like carbon (DLC) films were deposited onto a steel substrate. By using the plasma immersion ion implantation (PIII) technique, a nitrogen layer was formed on the steel surface before depositing the DLC films. This PIII formed nitrogen layer, which acts as the buffer layer, has apparently increased the adhesion between the DLC film and the steel substrate. The microstructures, the nanomechanical properties, and the adhesion of the DLC were investigated by the techniques of X-ray diffraction (XRD), transmission electron microscopy (TEM), nanoindentation, and nanoscratch. Results show that the hardness and Young's modulus were significantly improved, up to 2 to 9 times; while the implantation depth and the microstructure of the nitrogen layers vary with nitrogen/hydrogen ratio (N:H = 1:0, 1:1, 1:3). Raman analyses indicate that the I(D)/I(G) ratio increases with the thickness of DLC film. By using the PIII technique in the steel substrate, the adhesion of the DLC film onto the substrate is greatly enhanced, and wear resistance is elevated if the DLC film is sufficiently thick.