The effects of pulse frequency and substrate bias to the mechanical properties of CrN coatings deposited by pulsed DC magnetron sputtering

The chromium nitride coatings have been prepared by the bipolar symmetric pulsed DC magnetron reactive sputtering process at 2 kHz and 20 kHz pulse frequencies, respectively. Different substrate bias was applied with a pulsed DC bias unit with 50 kHz pulse frequency. Oscilloscope traces of the I–V waveforms indicate high power and high current density outputs during the symmetric bipolar pulsed mode. It is concluded that the (200) orientation of CrN films is observed. The grain size decreases with increasing pulse frequency and substrate bias. The substrate bias has a strong influence on the mechanical properties of CrN films. The scratch tests of the CrN coatings show that almost only tiny chipping failure is occurred. Sufficient adhesion strength quality of the coating is also observed. The substrate bias for the deposition of CrN films with sufficient hardness and adhesion properties combination is − 290 V at 20 kHz and − 408 V at 2 kHz pulse frequency, respectively.