Aggregation of nanoscale iron oxyhydroxides and corresponding effects on metal uptake, retention, and speciation: I. Ionic-strength and pH

With increasing aggregation by both pH and ionic strength, the proportion of introduced zinc adsorbed to the iron oxyhydroxide nanoparticles progressively decreased from 45% on the monodispersed control particles to as low as 16% on the aggregates, while the proportion of introduced zinc retained upon desorption (obtained by lowering the suspension pH) increased from 7% on the control particles to as much as 17% on the aggregated particles. Copper exhibited a subtler trend of only slightly declining uptake (from 43% to 36%) and retention (from 35% to 30%) with increasing aggregation state. EXAFS analysis was consistent with the macroscopic results, showing relatively little change in Cu speciation between samples analyzed before and after the desorption step but significant increases in Zn-Fe interatomic distances and coordination numbers after desorption. This suggests the presence of both strongly- and weakly-bound zinc ions; the latter are likely affiliated with less stable, more distorted surface sorption sites and are thus more readily desorbed, resulting in the retention of zinc that is bound to more stable, less-distorted sorption sites. For both metals, inner-sphere bidentate sorption appears to dominate the sorption process to the nanoparticle aggregates, with potential structural incorporation into the aggregates themselves.