Argon diffusion in Apollo 16 impact glass spherules: Implications for 40Ar/39Ar dating of lunar impact events

The 40Ar/39Ar technique applied to impact glass has been used to date both terrestrial and lunar impact events. The ability to utilize the 40Ar/39Ar technique rests on the assumption that impact glasses are closed to the loss of daughter product, 40Ar∗, after formation. Diffusion experiments were performed on three Apollo 16 lunar impact glasses and yielded activation energies for 39Ar of ∼17 to 20 kcal mol−1 and log10(D0/a2) values of −5.2 to −6.0 s−1. The resulting diffusion coefficients are interpreted as minimum values and the Apollo 16 glass is probably some of the least retentive of lunar glasses, as the degree of non-bridging oxygen is at one end of the range in lunar glasses. At temperatures below the glass transition temperature (i.e., ∼660 °C), the data can be explained by volume diffusion from a single diffusion domain. Modeling shows that Apollo 16 composition glass could lose significant quantities of radiogenic argon (40Ar∗) (∼90-100% over 20-40 Myr assuming a diffusion domain size (a) of 75 μm) due to diurnal temperature variations on the lunar surface, although 40Ar∗ loss is highly sensitive to exposure duration and effective diffusion domain size. Modeling shows that loss from transient thermal events (e.g., heating to ∼200 °C for 102 yr duration) can also cause partial resetting of apparent 40Ar/39Ar ages. In small (a = 75 μm) glasses a maximum of 50-60% of 40Ar∗ is lost over 4 Ga when buried to depths corresponding to temperatures of −15 °C. Results indicate that caution should be exercised in interpreting lunar impact glass 40Ar/39Ar ages, as the assumption of closed system behavior may have been violated, particularly in glasses with low fractions of non-bridging oxygen.