Experimental investigation of condensation predictions for dust-enriched systems

Condensation models describe the equilibrium distribution of elements between coexisting phases (mineral solid solutions, silicate liquid, and vapor) in a closed chemical system, where the vapor phase is always present, using equations of state of the phases involved at a fixed total pressure (<1 bar) and temperature (T). The VAPORS code uses a CaO-MgO-Al2O3-SiO2 (CMAS) liquid model at T above the stability field of olivine, and the MELTS thermodynamics algorithm at lower T. Quenched high-T crystal + liquid assemblages are preserved in meteorites as Type B Ca-, Al-rich inclusions (CAIs), and olivine-rich ferromagnesian chondrules. Experimental tests of compositional regions within 100 K of the predicted T of olivine stability may clarify the nature of the phases present, the phase boundaries, and the partition of trace elements among these phases. Twenty-three Pt-loop equilibrium experiments in seven phase fields on twelve bulk compositions at specific T and dust enrichment factors tested the predicted stability fields of forsteritic olivine (Mg2SiO4), enstatite (MgSiO3), Cr-bearing spinel (MgAl2O4), perovskite (CaTiO3), melilite (Ca2Al2SiO7-Ca2Mg2Si2O7) and/or grossite (CaAl4O7) crystallizing from liquid. Experimental results for forsterite, enstatite, and grossite are in very good agreement with predictions, both in chemistry and phase abundances. On the other hand the stability of spinel with olivine, and stability of perovskite and gehlenite are quite different from predictions. Perovskite is absent in all experiments. Even at low oxygen fugacity (IW-3.4), the most TiO2-rich experiments do not crystallize Al-, Ti-bearing calcic pyroxene. The stability of spinel and olivine together is limited to a smaller phase field than is predicted. The melilite stability field is much larger than predicted, indicating a deficiency of current liquid or melilite activity models. In that respect, these experiments contribute to improving the data for calibrating thermodynamic models including MELTS.