Crack severity in relation to non-homogeneous Ni oxidation in anode-supported solid oxide fuel cells
Keywords: پیلسوختی اکسید جامد ; Ni–YSZ anode; Ni oxidation; Redox cycling; Solid oxide fuel cell (SOFC); Electrolyte cracking